| Items |
 /Asset/Titanium-Plate.jpg 410S-1875-48-96 Stainless Steel Plate - Type 410S |
/Asset/Titanium-Plate.jpg 410S-1875-48-120 Stainless Steel Plate - Type 410S |
/Asset/Titanium-Plate.jpg 410S-1875-48-144 Stainless Steel Plate - Type 410S |
/Asset/Titanium-Plate.jpg 410S-1875-48-240 Stainless Steel Plate - Type 410S |
/Asset/Titanium-Plate.jpg 410S-1875-96-240 Stainless Steel Plate - Type 410S |
|||||
| Material | Type 410S Stainless Steel | |||||||||
| Shapeform | Plates | |||||||||
| Thickness | 3/16 inches | |||||||||
| Thickness | 0.1875 inches4.7625 mm | |||||||||
| Size | 48 x 96 inches | 48 x 120 inches | 48 x 144 inches | 48 x 240 inches | 96 x 240 inches | |||||
| Width | 48 inches | 48 inches | 48 inches | 48 inches | 96 inches | |||||
| Length | 96 inches | 120 inches | 144 inches | 240 inches | 240 inches | |||||
| Plate Weight per Unit Area | 8.579 lbs/ft²41.882678 kg/m² | |||||||||
| Weight per Plate | 275 lbs124.73791 kg | 343 lbs155.5821932 kg | 412 lbs186.8800688 kg | 686 lbs311.1643864 kg | 1373 lbs622.7823652 kg | |||||
| Finish | No. 2B | |||||||||
| Condition | Hot Rolled Annealed Pickled | |||||||||
| Nominal Composition | 0 or trace Nickel 0.06 to 0.35% Carbon 0.75% Max. Titanium x Carbon Min 1.00% Max. Manganese 1.00% Max. Silicon 10.50 to 11.75% Chrominum | |||||||||
| ASTM Specification | ASME SA-240 ASTM A240 ASTM A480 UNS S41008 | |||||||||
| Steel Alloy Group | Ferritic | |||||||||
| Magnetic Properties | Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | Med. to High | |||||||||
| Hardness | Low | |||||||||
| Strength | Low | |||||||||
| Ductility | Med. | |||||||||
| Toughness | Low to Med. | |||||||||
| Elec. Conductance | Med. | |||||||||
| Thermal Conductance | Med. | |||||||||
| Thermal Expansion | Med. | |||||||||
| Heat Resistance (Scaling Strength) | High/Low | |||||||||
| Yield Strength | 49000 lbs/in² | |||||||||
| Tensile Strength | 70000 lbs/in² | |||||||||
| Elongation percent in 2 inches | 31 % | |||||||||
| Hardness (Rockwell B) | 85 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 9000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 4200 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 4000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 1000 lbs/in² | |||||||||
| Density | 0.28 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 29.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.11 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 14.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 16.6 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 9.3 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.5 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 10.3 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.7 x 10-6 ºF | |||||||||
| Melting Point Range | 2700 to 2750 ºF | |||||||||
| Electrical Resistivity | 57 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1250 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1400 ºF | |||||||||
| Welding Properties | Fair-Preheat 400-500°F, Anneal 1250°F after welding | |||||||||
| Drawing and Stamping | Fair-Good | |||||||||
| Hot Working - Initial Forging | 2000 to 2200 ºF | |||||||||
| Annealing Temp. | 1500 to 1650 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||