| Material | Type 310S Stainless Steel | |||||||||
| Shapeform | Sheets | |||||||||
| Thickness | 16 gauge | 16 gauge | 14 gauge | 14 gauge | 12 gauge | |||||
| Thickness | 0.060 inches1.524 mm | 0.060 inches1.524 mm | 0.075 inches1.905 mm | 0.075 inches1.905 mm | 0.105 inches2.667 mm | |||||
| Size | 48 x 96 | 48 x 120 | 48 x 96 | 48 x 120 | 48 x 96 | |||||
| Width | 48 | |||||||||
| Length | 96 | 120 | 96 | 120 | 96 | |||||
| Sheet Weight per Unit Area | 2.520 lbs/ft²12.30264 kg/m² | 2.520 lbs/ft²12.30264 kg/m² | 3.150 lbs/ft²15.3783 kg/m² | 3.150 lbs/ft²15.3783 kg/m² | 4.411 lbs/ft²21.534502 kg/m² | |||||
| Estimated Weight per Sheet | 80.65 lbs36.53445 kg | 100.81 lbs45.66693 kg | 100.81 lbs45.66693 kg | 126.01 lbs57.08253 kg | 141.14 lbs63.93642 kg | |||||
| Finish | No. 2B | |||||||||
| Condition | Cold Rolled Annealed | |||||||||
| Nominal Composition | 0.08% Max. Carbon 1.50% Max. Silicon 19.00 to 22.00% Nickel 2.00% Max. Manganese 24.00 to 26.00% Chrominum | |||||||||
| ASTM Specification | ASTM A240 ASTM A480 ASTM SA-240 UNS S31008 | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | Low | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 17000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 13000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 9000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 5000 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 28.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 8.2 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 10.8 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 8.8 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.0 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 9.4 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 9.7 x 10-6 ºF | |||||||||
| Melting Point Range | 2550 to 2650 ºF | |||||||||
| Electrical Resistivity | 78 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 2100 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1900 ºF | |||||||||
| Welding Properties | Good-Tough Welds | |||||||||
| Drawing and Stamping | Fair | |||||||||
| Hot Working - Initial Forging | 2000 to 2500 ºF | |||||||||
| Annealing Temp. | 1900 to 2100 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||