Aluminum Sheet and Coil - Series 1100-0

Unit of Measure

Items	1100-0-020-36-C Aluminum Sheet and Coil - Series 1100-0	1100-0-020-96 Aluminum Sheet and Coil - Series 1100-0	1100-0-025-36-C Aluminum Sheet and Coil - Series 1100-0	1100-0-025-96 Aluminum Sheet and Coil - Series 1100-0	1100-0-032-36-C Aluminum Sheet and Coil - Series 1100-0
Material	N/A Aluminum
Shapeform	N/A Coil	N/A Sheets	N/A Coil	N/A Sheets	N/A Coil
Series	N/A 1100-0
Grade	N/A 1100
Preparation	N/A Paper Interleaved
Temper	N/A Soft Temper
Finish	N/A Mill
Thickness	N/A 0.02 inches0.508 mm	N/A 0.02 inches0.508 mm	N/A 0.025 inches0.6350 mm	N/A 0.025 inches0.6350 mm	N/A 0.032 inches0.8128 mm
Size	N/A 36 x Coil	N/A 36 x 96	N/A 36 x Coil	N/A 36 x 96	N/A 36 x Coil
Width	N/A 36
Length	N/A	N/A 96	N/A	N/A 96	N/A
Sheet Weight per Unit Area	N/A 0.282 lbs/ft²1.377 kg/m²	N/A	N/A 0.353 lbs/ft²1.723 kg/m²	N/A	N/A 0.452 lbs/ft²2.207 kg/m²
Weight per Sheet	N/A	N/A 6.77 lbs3.071 kg	N/A	N/A 8.47 lbs3.842 kg	N/A
Coil Weight per Length	N/A 0.847 lbs/ft1.260 kg/m	N/A	N/A 1.058 lbs/ft1.574 kg/m	N/A	N/A 1.355 lbs/ft2.016 kg/m
ASTM Specification	N/A AMS 4001 AMS 4003 AMS-QQ-A-250/1 ASME SB-209 ASTM B209
Ultimate Strength	N/A 13 ksi
Yield Strength	N/A 5 ksi
Elongation percent in 2 inches	N/A 35
Hardness Brinnel Number	N/A 23
Ultimate Shearing Strength	N/A 9 ksi
Fatigue Endurance Limit¹	N/A 5 ksi
Modulus of Elasticity²	N/A 10.0 x 10⁶ ksi
Resistance to Corrosion - General³	N/A A
Stress Corrosion Cracking⁴	N/A A
Workability (Cold)⁵	N/A A
Mechinability	N/A E
Brazeability⁶	N/A A
Gas Weldability⁷	N/A A
Arc Weldability⁸	N/A A
Resistance Spot and Seam Weldability⁹	N/A B
Applications	N/A Sheet metal work, spun hollowware, fin stock
Density	N/A 0.098 lbs/in³
Specific Gravity	N/A 2.71
¹ Based on 500000.000 cycles of completely reversed stress using the R. R. Moore-type of machine and specimen. ² Average of tension and compression moduli. Compression modulus is about 2 percent greater than tension modulus. ³ Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on faying surfaces. ⁴ Stress-corrosion cracking ratings are based on service experience and on laboratory tests of specimens exposed to the 3.5% sodium chloride alternate immersion test. ⁵ Ratings A through D for Workability (cold), and A through E for Machinability, are relative ratings in decreasing order of merit. ⁶ Ratings A through D for Weldability and Brazeability are relative ratings. ⁷ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁸ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties. ⁹ A = Generally weldable by all commercial procedures and methods. B = Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance. C = Limited weldability because of crack sensitivity or loss in resistance to corrosion and mechanical properties.