| Items |
 304HB-1875 Hexagon Stainless Steel Bar - Type 304 |
304HB-250 Hexagon Stainless Steel Bar - Type 304 |
304HB-375 Hexagon Stainless Steel Bar - Type 304 |
304HB-4375 Hexagon Stainless Steel Bar - Type 304 |
304HB-500 Hexagon Stainless Steel Bar - Type 304 |
|||||
| Material | Type 304 Stainless Steel | |||||||||
| Shapeform | Hexagon Bar | |||||||||
| Size | 3/16 inches | 1/4 inches | 3/8 inches | 7/16 inches | 1/2 inches | |||||
| Size | 0.1875 inches4.7625 mm | 0.25 inches6.35 mm | 0.375 inches9.525 mm | 0.4375 inches11.1125 mm | 0.5 inches12.7 mm | |||||
| Weight | 0.1035 lbs/ft0.154008 kg/m | 0.1841 lbs/ft0.2739408 kg/m | 0.4142 lbs/ft0.6163296 kg/m | 0.5637 lbs/ft0.8387856 kg/m | 0.7363 lbs/ft1.0956144 kg/m | |||||
| Weight per 12' Length | 1.242 lbs0.562626 kg | 2.209 lbs1.000677 kg | 4.970 lbs2.25141 kg | 6.765 lbs3.064545 kg | 8.835 lbs4.002255 kg | |||||
| Finish | No. 2B | |||||||||
| Condition | Cold Drawn Annealed | |||||||||
| Nominal Composition | 0 to 0.25% Carbon 1.00% Max. Silicon 2.00% Max. Manganese 6 to 36% Nickel 7 to 30% Chrome | |||||||||
| ASTM Specification | ASTM A276 UNS S30400 | |||||||||
| Random Length | 10 to 14 ft | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Yield Strength | 46000 lbs/in² | |||||||||
| Tensile Strength | 89000 lbs/in² | |||||||||
| Elongation percent in 2 inches | 55 % | |||||||||
| Hardness (Rockwell B) | 86 | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1000°F | 17000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1100°F | 12000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1200°F | 7000 lbs/in² | |||||||||
| Creep Strength Load for 10000 Hr. with 1% Elongation at 1300°F | 4000 lbs/in² | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 28.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 9.6 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.9 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 10.2 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.4 x 10-6 ºF | |||||||||
| Melting Point Range | 2550 to 2650 ºF | |||||||||
| Electrical Resistivity | 72 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1650 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1500 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Very Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||