| Items |
 317L-28-36-C Stainless Steel Sheet and Coil - Type 317L |
317L-26-36-C Stainless Steel Sheet and Coil - Type 317L |
317L-26-48-C Stainless Steel Sheet and Coil - Type 317L |
317L-24-30-C Stainless Steel Sheet and Coil - Type 317L |
317L-24-36-C Stainless Steel Sheet and Coil - Type 317L |
|||||
| Material | Type 317L Stainless Steel | |||||||||
| Shapeform | Coil | |||||||||
| Thickness | 28 gauge | 26 gauge | 26 gauge | 24 gauge | 24 gauge | |||||
| Thickness | 0.015 inches0.381 mm | 0.0178 inches0.45212 mm | 0.0178 inches0.45212 mm | 0.0235 inches0.5969 mm | 0.0235 inches0.5969 mm | |||||
| Size | 36 x Coil | 36 x Coil | 48 x Coil | 30 x Coil | 36 x Coil | |||||
| Width | 36 | 36 | 48 | 30 | 36 | |||||
| Length | ||||||||||
| Sheet Weight per Unit Area | 0.630 lbs/ft²3.07566 kg/m² | 0.76 lbs/ft²3.71032 kg/m² | 0.76 lbs/ft²3.71032 kg/m² | 1.008 lbs/ft²4.921056 kg/m² | 1.008 lbs/ft²4.921056 kg/m² | |||||
| Estimated Weight per Sheet | ||||||||||
| Finish | No. 2B No. 3 No. 4 | |||||||||
| Condition | Cold Rolled Annealed | |||||||||
| Nominal Composition | 0.08% Max. Carbon 1.00% Max. Silicon 11.00 to 15.00% Nickel 18.00 to 20.00% Chrominum 2.0 to 3.0% Molybdenum 2.00% Max. Manganese | |||||||||
| ASTM Specification | ASTM A240 ASTM A262 Prac E ASTM A480 ASTM SA-240 UNS S31700 | |||||||||
| Steel Alloy Group | Austenitic | |||||||||
| Magnetic Properties | Non-Magnetic | |||||||||
| Harden By | Cold Work | |||||||||
| Corrosion Resistance | High | |||||||||
| Hardness | Low to Med. | |||||||||
| Strength | Low to Med. | |||||||||
| Ductility | High | |||||||||
| Toughness | High | |||||||||
| Elec. Conductance | Low | |||||||||
| Thermal Conductance | Low | |||||||||
| Thermal Expansion | High | |||||||||
| Heat Resistance (Scaling Strength) | High/High | |||||||||
| Density | 0.29 lbs/in³ | |||||||||
| Modulus of Elasticity in Tension | 28.0 x 106 lbs/in² | |||||||||
| Specific Heat (32 to 212°F) | 0.12 BTU/ºF/lbs | |||||||||
| Thermal Conductivity at 212°F | 9.4 BTU/hr.ft²/ft/ºF | |||||||||
| Thermal Conductivity at 932°F | 12.4 BTU/hr.ft²/ft/ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 212°F) | 8.9 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 600°F) | 9.0 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1000°F) | 9.7 x 10-6 ºF | |||||||||
| Mean Coefficient of Thermal Expansion per °F (32 to 1200°F) | 10.3 x 10-6 ºF | |||||||||
| Melting Point Range | 2500 to 2550 ºF | |||||||||
| Electrical Resistivity | 74 µΩ.cm | |||||||||
| Max. Operating Temp. (Continuous Service) | 1700 ºF | |||||||||
| Max. Operating Temp. (Intermittent Service) | 1600 ºF | |||||||||
| Welding Properties | Very Good-Tough Welds | |||||||||
| Drawing and Stamping | Good | |||||||||
| Hot Working - Initial Forging | 2100 to 2300 ºF | |||||||||
| Annealing Temp. | 1850 to 2050 ºF | |||||||||
| Stress Relieving Temp. | 400 to 750 ºF | |||||||||
| Applications |
|
|||||||||
|
|
||||||||||